反応式
[B:1]([OH:4])([OH:3])[OH:2].[N:5]1[C:12]([NH2:13])=[N:11][C:9]([NH2:10])=[N:8][C:6]=1[NH2:7].C(=O)([O-])[O-].[Ca+2]>>[B:1]([OH:4])([OH:3])[OH:2].[N:5]1[C:12]([NH2:13])=[N:11][C:9]([NH2:10])=[N:8][C:6]=1[NH2:7]参加物
4
実験手順
First, 70 kg of orthoboric acid, 50 kg of melamine, and 1 kg of calcium carbonate were mixed by a Henschel mixer. Next, the mixture was placed in a constant temperature and humidity chamber at a temperature of 80° C. and a relative humidity of 80% for 2 hours to produce melamine borate. Then, the melamine borate was subjected to calcination and crystallization in a batch atmosphere furnace under a nitrogen atmosphere at 1750° C. for 2 hours to yield boron nitride with a graphitization index (GI) of 3.95 and a specific gravity of 2.27 g/cm3. After that, grinding was adjusted to prepare D-6 with a volume-average particle diameter of 18.0 μm.
後処理
- customwas placed in a constant temperature and humidity chamber at a temperature of 80° C.
出典と根拠
- ORDレコード
- ord-befd201c3ed0481bac2f6a7af77149bc
- 出典データセット
- uspto-grants-2013_10
- 特許番号
- US08557905B2
関連ノート
読み込み中…