Calcium pyrophosphate (Ca2P2O7) → Tricalcium Phosphate

HRID 1064216

Reaktionsgleichung

O.O.[P:3]([O-:7])([O-:6])([O-:5])=[O:4].[Ca+2:8].[Ca+2].C1C2[C@@H]3C=C[C@H](C2C=C1)C3.[N+]([O-])([O-])=O.[Ca+2].[N+]([O-])([O-])=O.[O-:29][P:30]([O:33]P([O-])([O-])=O)(=[O:32])[O-:31].[Ca+2].[Ca+2]>OP([O-])([O-])=O.OP([O-])([O-])=O.[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O.[Mg+2].[Ca+2].[Ca+2].[Ca+2].[Ca+2].[Ca+2].[Ca+2].[Ca+2].[Ca+2].[Ca+2].[Fe+2]>[P:3]([O-:7])([O-:6])([O-:5])=[O:4].[Ca+2:8].[P:30]([O-:33])([O-:32])([O-:31])=[O:29].[Ca+2:8].[Ca+2:8]

Komponenten

Reaktionsbedingungen

Temperatur: 500 °C

Versuchsvorschrift

Example 1 was repeated with the addition of 10.00 g dicalcium phosphate dihydrate, DCPD, CaHPO4.2H2O (Aldrich Chemical Co., Inc. #30,765-3, CAS #7789-77-7) to the homogeneous solution following endothermic dissolution of the calcium nitrate salt. The DCPD was present both as suspended solids and as precipitated material (no agitation used). Warming of the sample to >25° C. initiated an exothermic reaction as described in Example 1, resulting in the formation of a white, pasty solid. Heat treatment and X-ray diffraction of this solid were conducted as described in Example 1. Following heat treatment in air at 500° C. for 1 hour, XRD indicated the solid to be composed of whitlockite as the primary phase along with calcium pyrophosphate (Ca2P2O7) as the secondary phase.

Aufarbeitung

customas precipitated material (no agitation
temperatureWarming of the sample to >25° C.
customan exothermic reaction
customresulting in the formation of a white, pasty solid
temperatureHeat treatment and X-ray diffraction of this solid

Quellen und Nachweise

ORD-Eintrag: ord-b289627c381046d18b8692193f8ae518
Quelldatensatz: uspto-grants-2005_11
DOI: 10.6084/m9.figshare.5104873.v1
Patentnummer: US06969501B2

Verknüpfte Notizen

Wird geladen…