Dimethyl isophthalate → 3,6-Dioxabicyclo(6.3.1)dodeca-1(12),8,10-triene-2,7-dione

HRID 1076943Notizen

Reaktionsgleichung

Reaktionsgleichung von HRID 1076943
[C:1]([O:13][CH3:14])(=[O:12])[C:2]1[CH:11]=[CH:10][CH:9]=[C:4]([C:5]([O:7][CH3:8])=[O:6])[CH:3]=1.[Sb]#[Sb].OCCOC(=O)CCCCC(OCCO)=O>C([O-])(=O)C.[Mn+2].C([O-])(=O)C.C(O)CO>[C:5]1(=[O:6])[O:7][CH2:8][CH2:14][O:13][C:1](=[O:12])[C:2]2=[CH:11][CH:10]=[CH:9][C:4]1=[CH:3]2

Komponenten

6

Edukt 3

HCID 15088Dimethyl isophthalateHCID 23967Antimony, mol. (Sb2)HCID 74340Bis(2-hydroxyethyl) adipate

Produkt 1

HCID 817903,6-Dioxabicyclo(6.3.1)dodeca-1(12),8,10-triene-2,7-dione

Reagenzien, Katalysatoren, Lösungsmittel 2

HCID 12525Manganous AcetateKatalysatorHCID 174Ethylene GlycolLösungsmittel

Versuchsvorschrift

Dimethyl isophthalate, 1.37 kg, and ethylene glycol, 0.92 kg, were charged into a reactor together with an ester exchange catalyst which was a mixture of 2.05 g manganese acetate and 1.35 g diantimony trixoide. The ester exchange reaction was carried out as described in Example 1, and 3.29 kg of bis(hydroxyethyl)adipate was added to the product thus obtained. The polymerization was carried out at 265°C. at 1 mm Hg pressure for 6 hours to provide a poly(ethylene isophthalate/adiphate) having a mol ratio of isophthalate to adipate of 33 to 67 and having an intrinsic viscosity of 0.56, as determined in a solvent mixture of 25 volume percent trifluoroacetic acid and 75 volume percent methylene chloride.

Aufarbeitung

  1. additionwas added to the product
  2. customthus obtained