Reaktionsgleichung
[C:1]([O:4][CH:5]=[CH2:6])(=[O:3])[CH3:2].[C:7]1(=[O:13])[O:12][C:10](=[O:11])[CH:9]=[CH:8]1.[CH2:14]([OH:17])[CH2:15][CH3:16]>>[C:1]([O:4][CH:5]=[CH2:6])(=[O:3])[CH3:2].[C:10]([O:17][CH2:14][CH2:15][CH3:16])(=[O:11])/[CH:9]=[CH:8]\[C:7]([O-:12])=[O:13]Komponenten
3
Reaktionsbedingungen
- Temperatur
- 90 °C
Versuchsvorschrift
To 160 g of vinyl acetate/maleic anhydride copolymer, prepared as described in Example 1A, was added 264.52 g of 1-propanol in a 500 ml kettle. This mixture was heated to 90° C. in a nitrogen atmosphere for 5 hours to effect esterification. After 5 hours, the alternating vinyl acetate/propyl maleate copolymer was obtained in a 50% solids solution. The solution was then cooled to 40° C. and product recovered. Analysis showed 46.86% solid in solution; a relative viscosity of 1.25 and a specific viscosity of 0.25, this product has a K value of 30.
Quellen und Nachweise
- ORD-Eintrag
- ord-96be82696e024a0f8925186728fb6a4f
- Quelldatensatz
- uspto-grants-1986_01
- Patentnummer
- US04567035
Verknüpfte Notizen
Wird geladen…