Toluene → tert-Butylacrylamide

HRID 1589775

Reaktionsgleichung

Reaktionsgleichung von HRID 1589775
C([C:5](=[CH2:9])[C:6]([NH2:8])=[O:7])(C)(C)C.[C:10]1([CH3:16])[CH:15]=CC=C[CH:11]=1.N(C(C)(C)C#N)=NC(C)(C)C#N>CCCCCC>[C:10]([NH:8][C:6](=[O:7])[CH:5]=[CH2:9])([CH3:16])([CH3:15])[CH3:11]

Komponenten

5

Edukt 3

HCID 1140Toluene2×HCID 6547AzobisisobutyronitrileHCID 18539458t-Butylacrylamide

Produkt 1

HCID 7877tert-Butylacrylamide

Reagenzien, Katalysatoren, Lösungsmittel 1

HCID 8058HexaneLösungsmittel

Reaktionsbedingungen

Temperatur
80 °C

Versuchsvorschrift

A mixture of 50.0 g of t-butylacrylamide and 250 ml of toluene was heated at 80° C. with stirring under a nitrogen atmosphere in a 500 ml three-necked flask. 10 ml of a toluene solution containing 500 mg of azobisisobutyronitrile was added thereto as a polymerization initiator thereby polymerization was initiated. After polymerization for 3 hours, the polymerization solution was cooled and poured into 1 liter of hexane. The solids thus-deposited were collected by filtration, washed with hexane and dried with heating under a reduced pressure to obtain 47.9 g of P-17.

Aufarbeitung

  1. additionwas added
  2. customas a polymerization initiator thereby polymerization
  3. customAfter polymerization for 3 hours
  4. temperaturethe polymerization solution was cooled
  5. filtrationThe solids thus-deposited were collected by filtration
  6. washwashed with hexane
  7. customdried
  8. temperaturewith heating under a reduced pressure
  9. customto obtain 47.9 g of P-17