Versuchsvorschrift
A mixture of 100 ml of tetrahydrofuran (THF) and 30 g of powdered polyhydroxystyrene (PHS) was added to a 250 ml three-necked flask equipped with a temperature probe, an overhead mechanical stirrer and a nitrogen inlet. The mixture stirred for 30 minutes to form a homogeneous solution before 5.0 g of tertiary butyl vinyl ether, 4.8 g of phenethyl alcohol and 140 mg of solid pyridinium-para-toluene sulfonate was added. A brief exotherm was observed followed by a temperature rise of 23° to 27° C. The solution was allowed to stir at 23° C. for 20 hours before 4 g of triethylamine solution (prepared by dissolving 2.31 g of triethylanine in 200 g of TBF) was added to the reaction mixture to quench the acid. The reaction mixture was stirred for additional 30 minutes. The polymer solution was drop-wise added to 1000 ml of de-ionized water under vigorous stirring. The precipitated solid polymer was isolated by filtration. The polymer was washed two times with 250 ml of de-ionized water. The polymer was dried under vacuum at 60° C. for 18 hours.
Aufarbeitung
- additionwas added to a 250 ml three-necked flask
- customequipped with a temperature probe, an overhead mechanical stirrer and a nitrogen inlet
Quellen und Nachweise
- ORD-Eintrag
- ord-ea06b2601e8e4c0d9091042afa530493
- Quelldatensatz
- uspto-grants-2000_10
- Patentnummer
- US06133412
Verknüpfte Notizen
Wird geladen…