Methyl Methacrylate → HCID 178418385, Verbindung
Beteiligte Stoffe
| Rolle | Name | HCID | Einwaage |
|---|---|---|---|
| Edukt | Methyl Methacrylate | HCID 6658 | — |
| Edukt | 1-Methoxy-2-propanol | HCID 7900 | — |
| Edukt | Diacetone Alcohol | HCID 31256 | — |
| Edukt | UV-328 | HCID 33263 | — |
| Edukt | Octrizole | HCID 62485 | — |
| Edukt | Octyl 3-(3-(2H-benzotriazol-2-yl)-5-tert-butyl-4-hydroxyphenyl)propanoate | HCID 9868461 | — |
| Produkt | HCID 178418385 | HCID 178418385 | — |
Reaktionsschritte
A coating solution was prepared containing 7 grams (g) of Elvacite 2041 PMMA, 79 g of 1-methoxy-2-propanol, 14 g of diacetone alcohol, 0.85 g of Tinuvin 384, 0.43 g of Tinuvin 328, 0.22 g of Cyasorb 5411, and 2 drops of BYK 331 surfactant. Thus, the solution contains 7% PMMA by total weight and 10% Tinuvin 384, 5% Tinuvin 328, and 2.5% Cyasorb 5411 based on solids. This solution was applied by flow coating onto 7 mil (177.8 μm) polycarbonate films 10 inches (25.4 cm) wide and 15 inches (38.1 cm) long, the solvent was flashed at 50° C. for 10 minutes, and the coated film was baked for 1 hour at 100° C. The top 5 inches (12.7 cm) of the films was discarded.
Herkunft & Nachweise
| DOI | 10.6084/m9.figshare.5104873.v1 |
|---|---|
| Patentnummer | US08525191B2 |
| Quelldatensatz | uspto-grants-2013_09 |
| ORD ID | ord-f0f27b3d5f4445b495693b4ff407852b |
| Quellennotiz | uspto-grants-2013_09 |