Glycolic Acid → Poliglecaprone
Reaktionsgleichung
[C:1]1(=[O:8])[O:7][CH2:6][CH2:5][CH2:4][CH2:3][CH2:2]1.[CH2:9]1[O:16][C:14](=[O:15])[CH2:13][O:12][C:10]1=[O:11].C(O)(=O)CO>>[C:1]1(=[O:8])[O:7][CH2:6][CH2:5][CH2:4][CH2:3][CH2:2]1.[CH2:9]1[O:16][C:14](=[O:15])[CH2:13][O:12][C:10]1=[O:11]Komponenten
4
Versuchsvorschrift
The CT-1 copolymer was prepared by the copolymerization of ε-caprolactone (0.625 mole) with glycolide (32.3 mmole) in the presence of glycolic acid (3.756 mmole) as the initiator and stannous octanoate (0.1247 mmole as 0.2M solution in toluene) as the catalyst. The polymerization was conducted in a mechanically stirred reactor under a dry nitrogen atmosphere at 150° C. for 6.25 hours. At the conclusion of the polymerization, as determined by GPC, traces of unreacted monomer were removed by distillation under reduced pressure. The composition of the purified polymer was verified by IR and NMR. The polymer was shown to melt at 55° C. as determined by DSC.