Reaktionsgleichung
[CH2:1]1[O:8][C:6](=[O:7])[CH2:5][O:4][C:2]1=[O:3].N(CCO)(CCO)[CH2:10][CH2:11]O>>[C:6]1(=[O:7])[O:8][CH2:1][CH2:2][CH2:11][CH2:10][CH2:5]1.[CH2:1]1[O:8][C:6](=[O:7])[CH2:5][O:4][C:2]1=[O:3]Komponenten
3
Versuchsvorschrift
The CT-1 copolymer was prepared by the copolymerization of c-caprolactone (0.625 mole) with glycolide (32.3 mmole) in the presence of triethanolamine (1.05 mmole) as the initiator and stannous octanoate (0.1247 mmole as 0.2M solution in toluene) as the catalyst. The polymerization was conducted in a mechanically stirred reactor under a dry nitrogen atmosphere at 150° C. for 8.0 hours. At the conclusion of the polymerization, as determined by GPC, traces of unreacted monomer were removed by distillation under reduced pressure. The composition of the purified polymer was verified by IR and NMR. The polymer was shown to melt at 61° C. as determined by DSC.
Aufarbeitung
- customAt the conclusion of the polymerization
- customwere removed by distillation under reduced pressure
- customto melt at 61° C.
Quellen und Nachweise
- ORD-Eintrag
- ord-2b8c1040f0854a1583af9ff30d580de9
- Quelldatensatz
- uspto-grants-2011_11
- Patentnummer
- US08057817B2