Water → Tetralead trioxide sulfate

HRID 1065198

反応式

HRID 1065198 の反応式
[Pb:1]=[O:2].O.[S:4](=[O:8])(=[O:7])([OH:6])[OH:5]>C(O)(=O)C>[O-2:5].[O-2:2].[O-2:5].[O-:7][S:4]([O-:8])(=[O:6])=[O:5].[Pb+2:1].[Pb+2:1].[Pb+2:1].[Pb+2:1]

参加物

5

反応物 3

HCID 962WaterHCID 1118Sulfuric AcidHCID 14827Lead monoxide2 回

生成物 1

HCID 9941248Tetralead trioxide sulfate

試薬・触媒・溶媒 1

HCID 176Acetic Acid溶媒

反応条件

温度
65 °C

実験手順

A TBL slurry was prepared according to the method disclosed in Japanese Patent Publication No. 1149/67. More specifically, 8.162 Kg of powdery lead monoxide (PbO-DP) was charged in a high-speed stirrer-equipped, 60-liter capacity vessel filled with 10 l of water, and high speed agitation was conducted for 10 minutes to disperse the powder sufficiently homogeneously and the dispersion was heated at 65° C. Then, 50.8 cc of an acetic acid solution having a concentration of 2.7 moles/liter was added as a catalyst, and 1306 cc of sulfuric acid having a concentration of 7 moles/liter was dropped to the lead monoxide slurry over a period of 40 minutes and aging was conducted under agitation at 65° C. for 60 minutes to form a slurry of needle crystals of tribasic lead sulfate (Sample No. TBL-Hl).

後処理

  1. customA TBL slurry was prepared
  2. additionto disperse the powder sufficiently homogeneously
  3. additionwas added as a catalyst
  4. waitaging was conducted under agitation at 65° C. for 60 minutes