Antimony pentoxide → Antimony pentoxide

HRID 1080595

反応式

HRID 1080595 の反応式
[O:1]=[Sb:2]([O:4][Sb:5](=[O:7])=[O:6])=[O:3].[N+]([O-])([O-])=[O:9].[In+3:12].[N+]([O-])([O-])=[O:14].[N+]([O-])([O-])=O>O>[OH-:1].[In+3:12].[OH-:9].[OH-:14].[O:1]=[Sb:2]([O:4][Sb:5](=[O:7])=[O:6])=[O:3]

参加物

5

反応物 2

HCID 14813Antimony pentoxideHCID 26265Indium nitrate2 回

生成物 2

HCID 14813Antimony pentoxideHCID 88636Indium hydroxide

試薬・触媒・溶媒 1

HCID 962Water溶媒2 回

実験手順

900 g of water was added to 600 g of the diantimony pentoxide sol (specific gravity: 1,198, Sb2O5 concentration: 18.4 wt %) prepared in Preparation Example 1 for dilution. Then, an aqueous indium nitrate solution having 242.2 g of indium nitrate (In(NO3)3.3H2O, In2O3 content: 39.1 wt %, guaranteed reagent, manufactured by Mitsuwa Kagaku Yakuhin K. K.) dissolved in 200 g of water, was added thereto with stirring at room temperature. Then, the mixture was heated at 90° C. for 6 hours to obtain a mixed slurry of indium hydroxide and diantimony pentoxide. This slurry had an In2O3 concentration of 4.9 wt %, a Sb2O5 concentration of 5.7 wt % and an In2O3 /Sb2O5 molar ratio of 1.0.

後処理

  1. customprepared in Preparation Example 1 for dilution
  2. additionwas added
  3. temperatureThen, the mixture was heated at 90° C. for 6 hours