Chromium oxide → Bismuth oxide antimony oxide chromium oxide
反応式
[Bi:1]=[O:2].[Sb:3]=[O:4].[B]=O.[O-2].[Cr+3:8].[O-2].[O-2].[Cr+3]>>[Bi:1]=[O:2].[Sb:3]=[O:4].[O-2:2].[Cr+3:8].[O-2:2].[O-2:2].[Cr+3:8]参加物
実験手順
A bismuth oxide powder (whose average particle size is about 2 to 3 μm), an antimony oxide powder (whose average particle size is about 2 to 3 μm) and a boron oxide fine powder (whose average particle size is about 2 to 3 μm) were mixed at a weight of 97.5:2:0.5. The mixed powder was heat treated at a temperature of 450° C. for 5 hrs. in the air. Further, a bismuth oxide powder a chromium oxide fine powder (whose average particle size is about 0.5 to 1.5 μm) were mixed at a weight ratio of 75:25. The mixed powder was heat treated at a temperature of 550° C. for 5 hrs. These were blended at a weight ratio of 10:1 and ground fine. Consequently, a synthetic powder of bismuth oxide/antimony oxide/chromium oxide (whose average particle size is about 2 to 3 μm) was obtained.
後処理
- temperatureThe mixed powder was heat
- additiontreated at a temperature of 450° C. for 5 hrs
- temperatureThe mixed powder was heat
- additiontreated at a temperature of 550° C. for 5 hrs
出典と根拠
- ORDレコード
- ord-cd0bf316cdaf486197c3b504e3af1e5f
- 出典データセット
- uspto-grants-1998_04
- 特許番号
- US05739742
反応ノート
読み込み中…