2-Vinylnaphthalene → Chloromethylstyrene 2-vinylnaphthalene

HRID 256302

反応式

HRID 256302 の反応式
[Cl:1][CH2:2][CH:3]=[CH:4][C:5]1[CH:10]=[CH:9][CH:8]=[CH:7][CH:6]=1.[CH:11]([C:13]1[CH:22]=[CH:21][C:20]2[C:15](=[CH:16][CH:17]=[CH:18][CH:19]=2)[CH:14]=1)=[CH2:12]>>[Cl:1][CH2:2][CH:3]=[CH:4][C:5]1[CH:10]=[CH:9][CH:8]=[CH:7][CH:6]=1.[CH:11]([C:13]1[CH:22]=[CH:21][C:20]2[C:15](=[CH:16][CH:17]=[CH:18][CH:19]=2)[CH:14]=1)=[CH2:12]

参加物

3

反応物 2

HCID 132302-VinylnaphthaleneHCID 94242Benzene, (3-chloro-1-propenyl)-

生成物 1

HCID 86741842Chloromethylstyrene 2-vinylnaphthalene収率 100%

実験手順

Four different polymer particles were prepared containing different proportions of monomers in the shell as shown in Table 7. Each preparation began with 50 mL of latex from Example 6A and 1 g of a mixture of chloromethylstyrene and 2-vinylnaphthalene in the appropriate ratio to produce 10, 30, 70, and 100 percent (w/w) chloromethylstyrene/2-vinylnaphthalene shells (lots 6.1, 6.2, 6.3, and 6.4, respectively, the latex from Example 6A having been designated as 6.0). For each preparation, 50 mg of potassium persulfate was used in one-hour polymerizations at 95°-100° C. The monomer conversions and optical densities at 340 nm of a 1:100 dilution in water of the polymer particle latices are also shown in Table 7; the solids content was 14%

後処理

  1. customFour different polymer particles were prepared
  2. additioncontaining different proportions of monomers in the shell