Ethylene → Ethene propene ethylidenenorbornene

HRID 431178

反応式

HRID 431178 の反応式
C=C.[CH:3](=[C:5]1[CH2:10][CH:9]2[CH2:11][CH:6]1[CH:7]=[CH:8]2)[CH3:4].[CH2:12]=[CH:13][CH3:14]>ClC1C=CC=CC=1Cl>[CH2:3]=[CH2:4].[CH2:12]=[CH:13][CH3:14].[CH:3](=[C:5]1[CH2:10][CH:9]2[CH2:11][CH:6]1[CH:7]=[CH:8]2)[CH3:4]

参加物

5

反応物 3

HCID 6325Ethylene2 回HCID 8252PropyleneHCID 27756Ethylidenenorbornene2 回

生成物 1

HCID 168253Ethene propene ethylidenenorbornene

試薬・触媒・溶媒 1

HCID 72391,2-Dichlorobenzene溶媒

実験手順

The procedure of Comparative Example 2 was followed except that the catalyst used was 5×10−7 mol of rac-[(ind)Et2PBCl2(ind)ZrCl2] activated with 5×10−3 mol of MAO. The internal pressure was raised by 2 bar with ethylene. The polymerization took place in the presence of 1 g of ethylidenenorbornene (ENB). The terpolymer formed (1.5 g) contained 63 wt. % of ethylene, 35 wt. % of propylene and 2 wt. % of ENB. The intrinsic viscosity in ortho-dichlorobenzene at 140° C. was 1.86 dl/g. The GC measurement in o-Cl2-benzene at 140° C. gave Mw=460 kg/mol and Mn=203 kg/mol. The DSC measurement in the 2nd heating indicated an amorphous polymer with a glass transition temperature Tg of −50° C.

後処理

  1. customThe terpolymer formed (1.5 g)
  2. customat 140° C.
  3. temperatureThe DSC measurement in the 2nd heating