Ethylene → Bicyclo[2.2.1]hept-2-ene, polymer with ethene

HRID 560947

反応式

HRID 560947 の反応式
[CH:1]12[CH2:7][CH:4]([CH2:5][CH2:6]1)[CH:3]=[CH:2]2.C=C.[H][H].C[Al]1CC[CH2:16][CH2:15]O1>[Cl-].[Cl-].C(=[Zr+2](C1C2C(CC=CC=2)CC1)C1C2C(CC=CC=2)CC1)(C)C>[CH:1]12[CH2:7][CH:4]([CH2:5][CH2:6]1)[CH:3]=[CH:2]2.[CH2:15]=[CH2:16]

参加物

6

反応物 4

HCID 6325Ethylene3 回HCID 103522-Norbornene2 回HCID 23511181MethylalumoxaneHCID 178418361HCID 178418361、化合物2 回

生成物 1

HCID 168460Bicyclo[2.2.1]hept-2-ene, polymer with ethene

試薬・触媒・溶媒 1

HCID 178461100HCID 178461100、化合物触媒

反応条件

温度
90 °C

実験手順

Norbornene, hydrocarbon-based solvent, ethylene and hydrogen was supplied to a continuous polymerization apparatus under the conditions that the norbornene concentration was 2.95 mol/L and the ethylene concentration was 1.05 mol/L and the ratio of hydrogen and ethylene was 0.21×10−3. At the same time, as the catalyst, racemic-isopropylidene-bis (tetrahydroindenyl) zirconium dichloride was supplied and, as a support catalyst, a catalyst system composed of methyalumoxane (10% toluene solution) was supplied to the reaction apparatus. The temperature of the reaction was maintained at 90° C. In the following step, the solvent was removed by high temperature and depressurization. The copolymer in a melt state was extruded in a strand shape, and the copolymer was cut into pellets having a length of 3 mm and a diameter of 2 mm. For the copolymerization, 0.6% antioxidant (trade name: Irganox 1010 manufactured by Chiba Special Chemicals Co. Ltd.) and 0.4% pentaerythritol tetrastearate were added.

後処理

  1. customIn the following step, the solvent was removed by high temperature and depressurization
  2. customFor the copolymerization, 0.6% antioxidant (trade name: Irganox 1010 manufactured by Chiba Special Chemicals Co. Ltd.) and 0.4% pentaerythritol tetrastearate
  3. additionwere added