Azobisisobutyronitrile → Vinylpyrrolidone lauryl methacrylate
関与物質
| 役割 | 名称 | HCID | 仕込み量 |
|---|---|---|---|
| 反応物 | Azobisisobutyronitrile | HCID 6547 | — |
| 反応物 | N-vinyl-2-pyrrolidone | HCID 6917 | — |
| 反応物 | Lauryl Methacrylate | HCID 8906 | — |
| 生成物 | Vinylpyrrolidone lauryl methacrylate | HCID 20459467 | — |
反応手順
The N-vinyl-2-pyrrolidone/lauryl methacrylate (6/94) copolymer was prepared in the following manner. In 100 parts of 0-grade Solvent L were placed 47 parts of lauryl methacrylate, 3 parts of N-vinyl-2-pyrrolidone and 0.2 parts of azobisisobutyronitrile (polymerization initiator). The mixture was reacted at 60 to 70° C. for about 12 hours at nitrogen atmosphere.