Melamine phosphate → HCID 178508833、化合物

HRID 840952ノート

反応式

HRID 840952 の反応式
[C:1]1([NH2:9])[N:6]=[C:5]([NH2:7])[N:4]=[C:3]([NH2:8])[N:2]=1.O[P:11](O)(O)=O>O>[N:2]1[C:3]([NH2:8])=[N:4][C:5]([NH2:7])=[N:6][C:1]=1[NH2:9].[P:11]

参加物

3

反応物 1

HCID 92612Melamine phosphate3 回

生成物 1

HCID 178508833HCID 178508833、化合物

試薬・触媒・溶媒 1

HCID 962Water溶媒

実験手順

Melamine polyphosphate and a process for preparing melamine polyphosphate are described, inter alia, in WO 97/44377. According to this reference, melamine polyphosphate having a solubility of 0.01 to 0.10 g per 100 ml water at 25° C., a pH between 2.5 and 4.5, and a melamine/phosphorus molar ratio of between 1.0 and 1.1, may be obtained as a 10 wt % aqueous slurry at 25° C. WO 97/44377 also describes a two-step process for preparing the disclosed melamine polyphosphate slurry. In the first step melamine, urea, and an aqueous orthophosphoric acid solution (containing at least 40 wt % orthophosphoric acid), are mixed to produce a reaction mixture having a melamine/orthophophoric acid molar ratio between 1.0 and 1.5 moles and a urea/orthophophoric acid molar ratio between 0.1 and 1.5 at a temperature between 0 and 140° C. The resulting reaction mixture is then stirred at a temperature between 0 and 140° C. and dehydrated to produce a powdery product comprising a double salt of orthophosphoric acid with melamine and urea. This powdery product is then heated to between 240 and 340° C. and maintained in this temperature range for between 0.1 and 30 hours while preventing agglomeration to obtain melamine polyphosphate.

後処理

  1. customat 25° C.

出典と根拠

ORDレコード
ord-ff02de2362974b35aa671113ed3a947d
出典データセット
uspto-grants-2002_04
特許番号
US06369137B2

反応ノート

読み込み中…