Isophthalic Acid → 1,2-Bis(4-hydroxyphenyl)ethane isophthalate
反応式
[C:1]([OH:12])(=[O:11])[C:2]1[CH:10]=[CH:9][CH:8]=[C:4]([C:5]([OH:7])=[O:6])[CH:3]=1.C(O[C:17]1[CH:22]=[CH:21][CH:20]=[CH:19][C:18]=1[CH2:23][CH2:24][C:25]1[CH:30]=[CH:29]C=[CH:27][C:26]=1OC(=O)C)(=O)C.[C:35](=[O:38])([O-])[O-].[K+].[K+]>>[C:1]([OH:12])(=[O:11])[C:2]1[CH:10]=[CH:9][CH:8]=[C:4]([C:5]([OH:7])=[O:6])[CH:3]=1.[OH:6][C:21]1[CH:20]=[CH:19][C:18]([CH2:23][CH2:24][C:25]2[CH:30]=[CH:29][C:35]([OH:38])=[CH:27][CH:26]=2)=[CH:17][CH:22]=1参加物
4
反応条件
- 温度
- 245 °C
実験手順
A charge consisting of 167 parts of isophthalic acid and 298 parts of 1,2-bis(acetoxyphenyl)ethane and 0.005 mols potassium carbonate per mol of 1,2-bis(acetoxyphenyl)ethane is placed in a reaction vessel equipped with a stirrer, condenser and receiver. The vessel is evacuated and purged with nitrogen three times. During the reaction a nitrogen blanket is maintained in the reactor. The temperature is raised to about 245° C. and acetic acid distills. The rate of distillation during the initial 67 percent of reaction is 1.82 ml mol-1 min.-1. The distillation rate tapers after 87 parts of acetic acid have distilled in 55 minutes. The temperature rises slowly to 270° C. during the initial stage. Thereupon the vessel is evacuated to a pressure of about 200 torr for about 5 minutes and the pressure is then slowly reduced to about 1 torr while the temperature is increased to about 290° C. When the amperage on the stirrer motor increases by 0.02 to 0.04 amps, the stirrer motor is switched off and the vacuum is released with nitrogen. A total of 112 parts of acetic acid (98 percent of theoretical) is collected. The rate of evolution of acetic acid during the vacuum stage is 1.67 ml mol-1 min.-1. The prepolymer is extruded from the vessel under slight nitrogen pressure and is reduced in a mill to a powder of particle size in the range of from 0.1 to 0.25 mm. The inherent viscosity of the prepolymer is 0.28. The prepolymer is off white in color.