Acrylonitrile → Butyl acrylate acrylonitrile

HRID 10486

반응식

HRID 10486 반응식
S([O-])(OCCCCCCCCCCCC)(=O)=O.[Na+].[C:19](#[N:22])[CH:20]=[CH2:21].[C:23]([O:27][CH2:28][CH2:29][CH2:30][CH3:31])(=[O:26])[CH:24]=[CH2:25]>O>[C:19](#[N:22])[CH:20]=[CH2:21].[C:23]([O:27][CH2:28][CH2:29][CH2:30][CH3:31])(=[O:26])[CH:24]=[CH2:25]

참가 물질

5

반응물 3

HCID 7855AcrylonitrileHCID 8846Butyl AcrylateHCID 3423265Sodium Lauryl Sulfate

생성물 1

HCID 168389Butyl acrylate acrylonitrile

시약·촉매·용매 1

HCID 962Water용매

반응 조건

온도
80 °C

실험 절차

Into a 2 L reactor equipped with an agitator, a thermometer, a nitrogen gas inlet tube, a dropping funnel, and a reflux condenser, was placed 600 g of distilled water, 0.71 g of sodium dodecyl sulfate as an emulsifier, and as monomers, 70 g of acrylonitrile and 30 g of n-butyl acrylate, and the reactor was nitrogen-purged while the reaction mixture was being stirred at 80° C. Next, 1.6 g of 4,4′-azobis(4-cyanovaleric acid) as a polymerization initiator together with 30 g of distilled water was added into the reactor, and a reaction was initiated. Stirring was performed at 80° C. for 10 hours, and an acrylonitrile/n-butyl acrylate random copolymer was produced with a conversion rate of monomers of 89%. GPC measurement confirmed that Mw=472,000, Mn=214,000, and Mw/Mn=2.21.

후처리

  1. customInto a 2 L reactor equipped with an agitator
  2. custompurged while the reaction mixture
  3. additionNext, 1.6 g of 4,4′-azobis(4-cyanovaleric acid) as a polymerization initiator together with 30 g of distilled water was added into the reactor
  4. stirringStirring

출처 및 근거

ORD 기록
ord-9012a462bfb94024b4c6414b67674db0
출처 데이터셋
uspto-grants-2006_08
특허 번호
US07094833B2