Palladium(II) nitrate dihydrate → Palladium nitrate

HRID 1811703

반응식

HRID 1811703 반응식
O.O.[N+:3]([O-:6])([O-:5])=[O:4].[Pd+2:7].[N+:8]([O-:11])([O-:10])=[O:9]>[Fe].O>[N+:3]([O-:6])([O-:5])=[O:4].[Pd+2:7].[N+:8]([O-:11])([O-:10])=[O:9]

참가 물질

4

반응물 1

HCID 44134881Palladium(II) nitrate dihydrate

생성물 1

HCID 24932Palladium nitrate

시약·촉매·용매 2

HCID 23925Iron촉매HCID 962Water용매

반응 조건

온도
70 °C

실험 절차

Powders of a metal getter having composition by weight of Zr 70%—V 24.6%—Fe 5.4% are sieved to recover a getter powder having a grain size fraction ranging from about 53 μm to about 128 μm. 100 g of this fraction is added to a solution prepared by dissolving 0.5 g of palladium nitrate dihydrate, Pd(NO3)2×2 H2O, in 40 ml distilled water in a glass flask. The flask is connected to a Rotavapor®, and the solution is heated to 70° C. and maintained for 5 hours of stirring, resulting in the evaporation of water and deposition of palladium nitrate onto the surface of the getter powder. The powders are then subjected to a thermal treatment at 500° C. under vacuum for 3 hours and allowed to cool to room temperature for about the next 16 hours. As a result, the palladium nitrate decomposes into metallic palladium that forms “islands” on the surface of the grains of the getter material. The nominal amount of palladium is equal to 0.2% by weight of the solid, composite getter.

후처리

  1. filtrationare sieved
  2. customto recover a getter powder
  3. addition100 g of this fraction is added to a solution
  4. customprepared
  5. distillationin 40 ml distilled water in a glass flask
  6. temperaturemaintained for 5 hours