Geniosil GF 92 → Ethylene butyl acrylate

반응식

C=C.[CH2:3]([O:7][C:8](=[O:11])[CH:9]=[CH2:10])[CH2:4][CH2:5][CH3:6].C(OCC1OC1)(=O)C(C)=C.C1(NCCC[Si](OC)(OC)OC)CCCCC1.N[SiH3]>>[CH2:3]=[CH2:4].[C:8]([O:7][CH2:3][CH2:4][CH2:5][CH3:6])(=[O:11])[CH:9]=[CH2:10]

참가 물질

반응물 3

HCID 76477Geniosil GF 92

HCID 6452341Ethylene n-butylacrylate glycidyl methacrylate

HCID 14094712CID 14094712

생성물 1

HCID 16212797Ethylene butyl acrylate

실험 절차

45 g. of an ethylene/n-butylacrylate/glycidyl methacrylate containing 4 wt. % GMA and 30 weight percent nBA and having a melt index of 1000 was reacted with 3.3 g. of N-cyclohexylaminopropyl trimethoxysilane in a Brabender mixer at 160° C. for 10 min. Rotor speed was 100 rpm. This represents a stoichiometric balance of aminosilane to the glycidyl moiety. The MI of the grafted product was 1098. This is above that of the direct copolymer which suggests that little or no crosslinking occurred during the preparation of the grafted copolymer.