[Al:1].[Mg:2].[S:3]([OH:13])(=[O:12])([C:5]1[CH:10]=[CH:9][C:8]([NH2:11])=[CH:7][CH:6]=1)=[O:4]>O>[S:3]([O-:13])(=[O:12])([C:5]1[CH:6]=[CH:7][C:8]([NH2:11])=[CH:9][CH:10]=1)=[O:4].[Al+3:1].[Mg+2:2].[S:3]([O-:13])(=[O:12])([C:5]1[CH:6]=[CH:7][C:8]([NH2:11])=[CH:9][CH:10]=1)=[O:4].[S:3]([O-:13])(=[O:12])([C:5]1[CH:6]=[CH:7][C:8]([NH2:11])=[CH:9][CH:10]=1)=[O:4].[S:3]([O-:13])(=[O:12])([C:5]1[CH:6]=[CH:7][C:8]([NH2:11])=[CH:9][CH:10]=1)=[O:4].[S:3]([O-:13])(=[O:12])([C:5]1[CH:6]=[CH:7][C:8]([NH2:11])=[CH:9][CH:10]=1)=[O:4]참가 물질
4
실험 절차
The powder prepared by Example 1 was calcined at 600° C. for 24 hrs in a high-temperature oven to form magnesium aluminum layered double oxide (LDO). Next, 30.06 g (1.5 times of the AEC of the magnesium aluminum layered double hydroxide) of sulfanilic acid salt (SAS) as a modifier was dissolved in 50 ml of water to form a modifier aqueous solution. 10 g of magnesium aluminum layered double oxide was then slowly added to the modifier aqueous solution and then the modifier aqueous solution was placed in a high-pressure autoclave to react at 100° C. overnight with agitation to form a mixture. The mixture was then washed with deionized water. After centrifugation for several times, the mixture was completely dried in a freeze-drying machine. The dried mixture was then milled to form magnesium aluminum sulfanilic acid salt (Mg—Al-SAS) layered double hydroxide powder. The XRD diffraction thereof is shown in FIG. 1.