Phosphorus oxide (P4O10) → 1,2,4,5-Benzenetetraamine

참여 물질

반응 조건

반응 단계

1,2,4,5-tetraaminobenzene tetrahydrochloride (1.7138 g, 6.033 mmol), 2-benzothiazole terephthalic acid (1.8059 g, 6.033 mmol) and 5.57 g of polyphosphoric acid (77% P2O5) were placed in a resin flask equipped with a mechanical stirrer, nitrogen inlet/outlet tubes, a vacuum connector and a side opening on the resin flask. The solution was heated at 90° C. in vacuo for 24 hours for dehydrochlorination. The reaction mixture was cooled to 60° C., then 4.04 g of P2O5 was added, in vacuo, thereby raising the polymer concentration to 18%. After adding the P2O5, heating was resumed. The reaction mixture was heated to 164° C., at which temperature the mixture became opalescent. The mixture was heated at 174° C. for 24 hours, then at 190° C. for 4 hours. Work-up, as in the preceeding Example, gave a polymer with [N]=7.5 dl/g, methanesulfonic acid at 30° C.