Acrylic Acid → Urethane acrylate

HRID 2259794

반응식

HRID 2259794 반응식
C[C@@]12[CH:10]([C:11]([C:13]([O-:15])=[O:14])=C)C[C@H](C1(C)C)CC2.C([O-])(=O)CCCCCCCCC[CH2:26][CH3:27].C([O-])(=O)CCCCCCCCCCC.C([Sn+2]CCCC)CCC.C(OCCO)(=O)C=C.[N-:61]=C=O.C(O)(=O)C=C.OC(C)(C)C(C1C=CC=CC=1)=O>C(OCC1OCCC1)(=O)C=C.C(O)C>[NH2:61][C:13]([O:15][CH2:26][CH3:27])=[O:14].[C:13]([OH:15])(=[O:14])[CH:11]=[CH2:10]

참가 물질

9

반응물 6

HCID 6581Acrylic AcidHCID 131652-Hydroxyethyl acrylateHCID 819842-Hydroxy-2-methyl-1-phenylpropan-1-oneHCID 105034IsocyanateHCID 9809426Di-n-butyldilauryltinHCID 92004758Isobomyl acrylate

생성물 1

HCID 21863578Urethane acrylate

시약·촉매·용매 2

HCID 702Ethanol용매HCID 94232Tetrahydrofurfuryl acrylate용매

반응 조건

온도
80 °C

실험 절차

An acrylate urethane oligomer composition was prepared in the following manner. A flask was charged with 202.8 g of PPG 1025 (polypropylene glycol with average molecular weight of 1025), 83.2 g of PPG 425 (polypropylene glycol with average molecular weight of 425), 221.6 g of isobornyl acrylate, 150.0 g of diphenylmethane 4,41 diisocyanate and 0.4 g of dibutyltin dilaurate. The mixture was heated at 80° C. for two hours. Hydroxyethyl acrylate, 23.2 g, was added and the heating continued for one hour. Ethanol, 9.7 g, was added and heating continued until the isocyanate band in the IR at 2268 cm-1 disappeared. The still warm product was diluted with 211.6 g of tetrahydrofurfuryl acrylate, 35.2 g acrylic acid and 35.2 g of Darocure 1173 initiator which is 2-hydroxy-2-methyl-1-phenyl-propane-1-one, a product of Ciba-Geigy. After thoroughly mixing, the mixture was poured warm into an opaque container. The yield of colorless product was 973 g with a viscosity of 8100 cP.

후처리

  1. temperatureheating
  2. additionAfter thoroughly mixing
  3. additionthe mixture was poured
  4. temperaturewarm into an opaque container

출처 및 근거

ORD 기록
ord-c4c9dd2e963747218d6ab6f32af6e9ea
출처 데이터셋
uspto-grants-1995_12
특허 번호
US05475038