참여 물질
| 역할 | 이름 | HCID | 투입량 |
|---|
| 반응물 | 4-Methoxyphenol | HCID 9015 | — |
| 반응물 | Toluene 2,4-Diisocyanate | HCID 11443 | — |
| 반응물 | 2,6-Di-tert-butyl-4-methylphenol | HCID 31404 | — |
| 반응물 | 2-Hydroxypropyl acrylate | HCID 61249 | — |
| 반응물 | Di-n-butyl diacetoxy tin | HCID 9798523 | — |
| 생성물 | Urethane acrylate | HCID 21863578 | — |
반응 단계
260 g (2 mol) of 2-hydroxypropyl acrylate (molecular weight 130) was placed in a flask equipped with a stirring blade, and with constant stirring, 174 g (1 mol) of TDI (2,4-tolylene diisocyanate) was added dropwise, with care taken over the generated heat, and the temperature was raised to 70° C. 1 g of dibutyl tin diacetate, 0.2 g of hydroquinone monomethyl ether and 1 g of 2,6-di-t-butyl-4-methylphenol were then added. Reaction was allowed to proceed at this temperature for 7 hours, and once the disappearance of NCO absorption had been confirmed via an infrared absorption spectrum, the reaction mixture was removed, yielding a urethane acrylate (A-X) as the radical polymerizable oligomer (A). The number average molecular weight of the synthesized urethane acrylate (A-X) was 434.
출처 및 근거
| DOI | 10.6084/m9.figshare.5104873.v1 |
|---|
| 특허 번호 | US06853788B2 |
|---|
| 출처 데이터셋 | uspto-grants-2005_02 |
|---|
| ORD ID | ord-fcd592e6641c4edf9c1358088911e541 |
|---|
| 출처 메모 | uspto-grants-2005_02 |
|---|