1-Butanol → Butan-1-ol;2-ethyl-2-(hydroxymethyl)propane-1,3-diol;titanium

참여 물질

반응 단계

A liquid mixture of 28.4 g (0.1 mole) of tetraisopropyl titanate, 4.5 g (0.033 mole) of trimethylolpropane, 0.1 g (0.0004 mole) of stearyl alcohol and an excess amount, i.e., 100 g (1.37 moles) of butanol was heated under reflux to dissolve the solid substance completely. The resultant isopropyl alcohol and butanol were then distilled off to obtain trimethylolpropane-butyl alcohol-titanate (polyol titanate). The polyol titanate was then cooled by ice, followed by an addition of butanol which contained 1.8002 g (0.10 mole) of water. After heating the resultant mixture to form a uniform solution, butanol was removed by distillation. Under cooling, butanol with 0.9005 g (0.05 mole) of water incorporated therein was added again. The resultant mixture was heated to effect polymerization and crosslinking. Butanol was then removed thoroughly under reduced pressure. After heating the residue again at 100° C. for 30 minutes in water-containing butanol, the product was dried under reduced pressure to obtain 12.2 g of a solid substance. This solid substance had such properties that it showed water repellency when water was added thereto but its surface was wet immediately when an alcohol was added thereto.

출처 및 근거