D-(+)-Cellobiose (CNP0226604.15) → Adipic Acid

HRID 429503

반응식

HRID 429503 반응식
C(O)[C@H]1O[C@@H](O[C@H]2[C@H](O)[C@@H](O)[C@H](O)O[C@@H]2CO)[C@H](O)[C@@H](O)[C@@H]1O.[C:24]([O:34]C)(=[O:33])[CH2:25][CH2:26][CH2:27][CH2:28][C:29]([O:31]C)=[O:30].CN(C1C=CC=CN=1)C.C(Cl)(=O)CCCCC(Cl)=O>O1CCOCC1>[C:24]([OH:34])(=[O:33])[CH2:25][CH2:26][CH2:27][CH2:28][C:29]([OH:31])=[O:30]

참가 물질

6

반응물 4

HCID 10712D-(+)-Cellobiose (CNP0226604.15)HCID 12329DimethyladipateHCID 218852-DimethylaminopyridineHCID 61034Adipoyl chloride

생성물 1

HCID 196Adipic Acid

시약·촉매·용매 1

HCID 312751,4-Dioxane용매

반응 조건

온도
50 °C

실험 절차

Five grams of resin (Mw of 50,000) synthesized from cellobiose and dimethyl adipate were poured into dioxane and then 3.7 g of dimethylaminopyridine and 3.0 g of adipic acid chloride were added dropwise thereto in a nitrogen atmosphere, followed by stirring for 20 hours at 50° C. A white powder, obtained from the resulting reaction mixture, was subjected to GPC. As a result, the molecular weight of the white powder was two to eight times larger than that of the resin measured before the reaction. The infrared absorption spectroscopy of the white powder revealed that the intensity of an absorption peak due to the C═O bond in the ester bond was higher than that shown in FIG. 8. Therefore, it was understood that esterification occurred in the saccharide portions in the resin of Example 1 and resulted in crosslinks by adipic acid.

후처리

  1. customA white powder, obtained from the resulting reaction mixture
  2. custommeasured before the reaction
  3. customThe infrared absorption spectroscopy of the white powder