O.[O:2]=[CH:3][C@@H:4]([C@H:6]([C@@H:8]([C@@H:10]([CH2:12][OH:13])[OH:11])[OH:9])[OH:7])[OH:5].[C:14]([O-:26])(=[O:25])[CH2:15][C:16]([CH2:21][C:22]([O-:24])=[O:23])([C:18]([O-:20])=[O:19])[OH:17].[NH4+:27].[NH4+].[NH4+]>>[C:14]([O-:26])(=[O:25])[CH2:15][C:16]([CH2:21][C:22]([O-:24])=[O:23])([C:18]([O-:20])=[O:19])[OH:17].[NH4+:27].[NH4+:27].[NH4+:27].[O:2]=[CH:3][C@@H:4]([C@H:6]([C@@H:8]([C@@H:10]([CH2:12][OH:13])[OH:11])[OH:9])[OH:7])[OH:5]참가 물질
실험 절차
Powdered dextrose monohydrate (1200 lbs) and powdered anhydrous citric acid (200 lbs) were combined in a 2000-gallon mixing tank that contained 215 gallons of soft water. To this mixture were added 42.3 gallons of 19% aqueous ammonia under agitation, and agitation was continued for approximately 30 minutes to achieve complete dissolution of solids. To the resulting solution were added 6 lbs of SILQUEST A-1101 silane to produce a pH˜8 solution (using pH paper), which solution contained approximately 41.7% dissolved dextrose monohydrate and dissolved ammonium citrate solids (as a percentage of total weight of solution); a 2-g sample of this solution, upon thermal curing at 400° F. for 30 minutes, would yield 25% solids (the weight loss being attributed to dehydration during thermoset binder formation). The solution was stirred for several minutes before being transferred to a binder hold tank from which it was used in the manufacture of glass fiber insulation, specifically, in the formation of a product called “pipe insulation uncured.”
출처 및 근거
- ORD 기록
- ord-3eccc05358f044b2a8c96f505e90bfcf
- 출처 데이터셋
- uspto-grants-2016_09
- 특허 번호
- US09434854B2
연결된 노트
불러오는 중…