참여 물질
| 역할 | 이름 | HCID | 투입량 |
|---|
| 반응물 | Methacrylic Acid | HCID 4093 | — |
| 반응물 | Styrene | HCID 7501 | — |
| 반응물 | Butyl Acrylate | HCID 8846 | — |
| 반응물 | Ammonium Persulfate | HCID 62648 | — |
| 반응물 | Sodium | HCID 5360545 | — |
| 반응물 | Methacrylic acid ethylene oxide | HCID 21880491 | — |
| 용매 | Water | HCID 962 | — |
| 생성물 | Methacrylic acid ethylene oxide | HCID 21880491 | — |
| 생성물 | Styrene-methacrylic acid butyl acrylate sodium | HCID 86591398 | — |
반응 단계
In a reactor equipped with a stirring bar and a thermometer, 683 parts by mass of water, 16 parts by mass of sodium salt of sulfate ester of methacrylic acid ethylene oxide adduct (ELEMINOL RS-30, manufactured by Sanyo Chemical Industries, Ltd.), 83 parts by mass of styrene, 83 parts by mass of methacrylic acid, 110 parts by mass of butyl acrylate and 1 part by mass of ammonium persulfate were charged, which was stirred at 400 rpm for 15 minutes, and a white emulsion was obtained. The emulsion was heated so that the system has a temperature of 75° C. and was subjected to a reaction for 5 hours. Further, 30 parts by mass of a 1-% by mass aqueous solution of ammonium persulfate were added, which was aged at 75° C. for 5 hours, and an aqueous dispersion solution of a vinyl resin (a copolymer of styrene-methacrylic acid-butyl acrylate-sodium salt of sulfate ester of methacrylic acid ethylene oxide adduct) [styrene-acrylic resin particle dispersion liquid] was obtained.
출처 및 근거
| DOI | 10.6084/m9.figshare.5104873.v1 |
|---|
| 특허 번호 | US09316938B2 |
|---|
| 출처 데이터셋 | uspto-grants-2016_04 |
|---|
| ORD ID | ord-b93de92b4a1c43a5be8ac8f154dd9bd8 |
|---|
| 출처 메모 | uspto-grants-2016_04 |
|---|