참여 물질
| 역할 | 이름 | HCID | 투입량 |
|---|
| 반응물 | Ammonia | HCID 222 | — |
| 반응물 | Carbon Dioxide | HCID 280 | — |
| 반응물 | Calcium Sulfate | HCID 24497 | — |
| 반응물 | Ammonium Carbonate | HCID 517111 | — |
| 반응물 | Calcium Hydroxide | HCID 6093208 | — |
| 반응물 | Methanedione--water (1/1) | HCID 22026445 | — |
| 생성물 | Calcium Carbonate | HCID 10112 | — |
| 생성물 | Ammonium Sulfate | HCID 6097028 | — |
반응 단계
The existing technology for preparation of nano calcium carbonate is bubbling carbon dioxide into a calcium hydroxide slurry to obtain nano calcium carbonate, while the present invention is injecting carbon dioxide into a calcium sulfate slurry containing ammonia to obtain nano calcium carbonate with byproduct ammonium sulfate. The principle of the present invention is as follows: due to the calcium hydroxide is more alkaline than ammonia, the reaction formula (1) cannot be carried out; instead, according to the reaction formula (2) and (3), the carbon dioxide is firstly reacted with ammonia to generate ammonium carbonate, and then ammonium carbonate and calcium sulfate react to get calcium carbonate and ammonium sulphate. The nano calcium carbonate can be obtained by controlling the speed of the formation of calcium carbonate. CaSO4+2NH3+2H2O→(NH4)2SO4+Ca(OH)2 (1) 2NH3+CO2+H2O→(NH4)2CO3 (2) (NH4)2CO3+CaSO4→(NH4)2SO4+CaCO3 (3)
출처 및 근거
| DOI | 10.6084/m9.figshare.5104873.v1 |
|---|
| 특허 번호 | US08846562B2 |
|---|
| 출처 데이터셋 | uspto-grants-2014_09 |
|---|
| ORD ID | ord-3523c3973ecd4e8dbe9df9f34b21dc67 |
|---|
| 출처 메모 | uspto-grants-2014_09 |
|---|