Chlorobenzene → 1,4-Diphenyl-1,3-butadiyne

참여 물질

반응 단계

A copolymer prepolymer of diphenylbutadiyne and p-diethynylbenzene was prepared in refluxing benzene solvent. The polymerization vessel was charged with 63 parts of diphenylbutadiyne, 2 parts of diethynylbenzene, 600 parts of benzene, and 2 parts of chlorobenzene. After heating to reflux, 2 parts of a catalyst mixture prepared by mixing 2 parts of nickel acetylacetonate and 4 parts of triphenylphosphine in 20 parts of benzene were added. After 1 hour, an additional 10 parts of diethynylbenzene was added. After 2 hours, 10 parts of diethynylbenzene and 2 parts of catalyst solution were added. After 3 hours, 20 parts of diethynylbenzene and 4 parts of catalyst solution were added. After a total reaction period of 7 hours, gas-liquid chromatographic analysis of the reaction mixture showed that 10% of each of the monomeric components remained. The solution was added to 5 times its volume of methanol, and 77 parts of the copolymer was precipitated. It had an acetylene content of 8.4% and an aromatic to olefin hydrogen ratio of 8:1.

출처 및 근거