Chloride → Acrylamide

HRID 849618

반응식

HRID 849618 반응식
[C:1]([NH2:5])(=[O:4])[CH:2]=[CH2:3].[Cl-:6].[C:7]([O:11][CH2:12][CH3:13])(=[O:10])[CH:8]=[CH2:9].C(N(CC(O)=O)CC(O)=O)CN(CC(O)=O)CC(O)=O.Cl.Cl.N(C(C1NCCN=1)(C)C)=NC(C1NCCN=1)(C)C>O>[C:1]([NH2:5])(=[O:4])[CH:2]=[CH2:3].[CH3:7][Cl:6].[C:7]([O:11][CH2:12][CH3:13])(=[O:10])[CH:8]=[CH2:9]

참가 물질

8

반응물 5

HCID 312ChlorideHCID 6049Ethylenediaminetetraacetic AcidHCID 6579AcrylamideHCID 8821Ethyl AcrylateHCID 99491012,2'-Azobis[2-(2-imidazolin-2-yl)propane] dihydrochloride

생성물 2

HCID 6579AcrylamideHCID 23497919MeCl EA

시약·촉매·용매 1

HCID 962Water용매

실험 절차

A 10% solution of poly(AMD/DMAEA.MeCl/EA) was prepared as follows: 13.87 parts of 53.58% aqueous acrylamide (AMD), 25.31 parts of a 80% aqueous solution of ethacryloxyethyltrimethylammonium chloride (DMAEA.NeCI), 2.33 parts of ethyl acrylate (EA), 0.3 part EDTA, 258.16 parts of deionized water and 0.030 parts of VA-044 were added to a suitable glass vessel. The solution was sparged with nitrogen gas and stirred for about one hour at ambient temperature. The nitrogen sparge was changed to a nitrogen purge, and polymerization was initiated thermally by raising the temperature of the solution to 44° C. Stirring and heating were continued for about 21 hours to give a clear, viscous solution of poly(AMD/DMAEA.MeCl/EA) having a standard viscosity of about 2.0 centipoise.

후처리

  1. customThe solution was sparged with nitrogen gas
  2. customThe nitrogen sparge
  3. custompurge
  4. custompolymerization
  5. temperatureby raising the temperature of the solution to 44° C
  6. stirringStirring
  7. temperatureheating
  8. waitwere continued for about 21 hours