Vinyl Chloride → Vinyl chloride-vinyl acetate

HRID 876099

반응식

HRID 876099 반응식
[CH:1]([Cl:3])=[CH2:2].[C:4]([O:7][CH:8]=[CH2:9])(=[O:6])[CH3:5].S(OOS([O-])(=O)=O)([O-])(=O)=O.[K+].[K+].C(OS(C1C=CC=CC=1)(=O)=O)CCCCCCCCCCC.[Na]>O>[C:4]([O:7][CH:8]=[CH2:9])(=[O:6])[CH3:5].[CH:1]([Cl:3])=[CH2:2]

참가 물질

6

반응물 4

HCID 6338Vinyl Chloride2회HCID 7904Vinyl AcetateHCID 24412Potassium PersulfateHCID 57371080Sodium dodecylbenzene sulphonate

생성물 1

HCID 61927Vinyl chloride-vinyl acetate

시약·촉매·용매 1

HCID 962Water용매

반응 조건

온도
60 °C

실험 절차

Deionized water (600 g), a monomer mixture composed of 438.8 g of a vinyl chloride monomer (97.5% by weight based on total charge monomer amount), 11.2 g of vinyl acetate (2.5% by weight based on total monomer charge amount), and 2.25 g of potassium persulfate were charged into a 2.5-L autoclave. The reaction mixture was stirred with a stirring blade while maintaining the rotation speed at 120 rpm, and the temperature of the reaction mixture was raised to 60° C. to start a polymerization. A 5% (by weight) aqueous solution of sodium dodecylbenzenesulfonate (180 g, 2% by weight based on total monomer charge amount) was continuously added from the start of the polymerization to 4 hr after the start of the polymerization, and the polymerization was stopped when the polymerization pressure was dropped by 0.6 MPa from a saturated vapor pressure of the vinyl chloride monomer at 60° C. Thereafter, the residual monomer was recovered to obtain a vinyl chloride-vinyl acetate emulsion.

후처리

  1. additionwere charged into a 2.5-L autoclave
  2. temperaturewhile maintaining the rotation speed at 120 rpm
  3. customa polymerization
  4. customafter the start of the polymerization
  5. customthe polymerization pressure
  6. customThereafter, the residual monomer was recovered