反应详情

温度

40 °C

To a 4000 ml polymerization apparatus dried under reduced pressure and thoroughly purged with nitrogen, 1740 ml of dry hexane, 50 g of 1-butene and triisobutylaluminum (1.0 mmol) were charged at normal temperature, then the temperature inside the polymerization apparatus was elevated to 40° C., and the polymerization apparatus was pressurized with propylene to 0.65 MPa and subsequently pressurized with ethylene to 0.80 MPa. Thereafter, a toluene solution in which 0.002 mmol of rac-dimethylsilylenebis(2-methyl-4-phenyl-indenyl)zirconium dichloride and methylaluminoxane (manufactured by Tosoh Finechem Corp.) in terms of 0.6 mmol of aluminum were contacted, was added to the polymerization vessel, and polymerization was conducted for 20 minutes while maintaining the internal temperature at 40° C. and the total pressure at 0.80 MPa by continuously supplying ethylene. The polymerization was stopped by adding 20 ml of methanol. After depressurizing, a polymer was precipitated out of the polymerization solution in 2 L of methanol, and was dried in a vacuum at 130° C. for 12 hours. The obtained polymer was 173.0 g and the polymerization activity was 259.5 kg/mmol-cat-hr. The polymer had a composition of 71.0 mol % of propylene content, 20.0 mol % of ethylene content and 9.0 mol % of 1-butene content, and had an intrinsic viscosity [η] of 2.78 dl/g.

1. customTo a 4000 ml polymerization apparatus
2. customdried under reduced pressure
3. additionwere charged at normal temperature
4. customwas elevated to 40° C.
5. additionwas added to the polymerization vessel, and polymerization
6. customa polymer was precipitated out of the polymerization solution in 2 L of methanol
7. customwas dried in a vacuum at 130° C. for 12 hours