反应详情

温度

120 °C

To 300 g of polyphosphoric acid (116% phosphoric acid) heated at 80°-95° C. was added 1.0 g (17.1 mmole) of sodium chloride followed by 50 g (0.12 mole) of 2,5-di(4-chloroanilino)terephthalic acid. The mixture was heated at 110°-115° C. for five hours. After the viscous solution was cooled to 90°-95° C., the acid strength was adjusted to 110.5% by the dropwise addition of 75% phosphoric acid. The resultant melt was stirred for 20 minutes and then slowly poured into a mixture of 324 g of methanol and 36 g of water (i.e., 90% aqueous methanol) at 35° C. The temperature of the resultant slurry was allowed to rise during the addition to about 64° C., with the temperature being controlled during addition by external cooling and adjustment of melt addition rate. The slurry was heated at reflux for one hour and diluted with 280 g of water. After the resultant slurry was stirred for 30 minutes, the solid component was collected by filtration and washed with water until acid-free. The press-cake was reslurried in water, the pH was adjusted to 8.5 using aqueous sodium hydroxide, and methanol was added. The resultant slurry was heated at about 120° C. in a closed system (e.g., a pressure reactor). After the slurry was cooled to ambient temperature, the solid component was collected by filtration and washed with water until neutral. The wet cake can be oven dried or used as is for specific applications. Here, the wet cake was dried in an oven at 60° C. to give about 43 g of 2,9-dichloroquinacridone as a brilliant magenta solid.

1. temperatureThe mixture was heated at 110°-115° C. for five hours
2. temperatureAfter the viscous solution was cooled to 90°-95° C.
3. additionto rise during the addition to about 64° C., with the temperature
4. additionbeing controlled during addition
5. temperatureby external cooling
6. additionadjustment of melt addition rate
7. temperatureThe slurry was heated
8. temperatureat reflux for one hour
9. stirringAfter the resultant slurry was stirred for 30 minutes
10. filtrationthe solid component was collected by filtration
11. washwashed with water until acid-free
12. additionwas added
13. temperatureAfter the slurry was cooled to ambient temperature
14. filtrationthe solid component was collected by filtration
15. washwashed with water until neutral
16. customdried
17. customHere, the wet cake was dried in an oven at 60° C.