Terpolymer 1 was produced by high-pressure polymerisation with free radical initiation, wherein ethylene monomers were reacted with vinyl trimethoxysilane (VTMS) and butylacrylate (BA) co-monomers amounts so as to yield 1.8 wt % (0.36 mol %) silane content and 17 wt % (4.4 mol %) BA content in final terpolymer 1, under the action of a radical initiator in a reactor at a high pressure of about 120 to 350 MPa and an elevated temperature of between 150 to 350° C. When the reaction was completed, the temperature and the pressure were lowered, and the resulting unsaturated polymer recovered.