Chromium oxide → Bismuth oxide antimony oxide chromium oxide boron oxide

A bismuth oxide powder (whose average particle size is about 2 to 3 μm), an antimony oxide fine powder (whose average particle size is about 2 to 3 μm), and a chromium oxide powder (whose average particle size is about 0.5 to 1.5 μm) were mixed at a weight ratio of 85:10:5. The mixed powder was heat treated at a temperature of 500° C. for 1 hr. Further, bismuth oxide fine particles and a boron oxide fine powder (whose average particle size is about 2 to 3 μm) were mixed at a weight ratio of 93:7. The mixed powder was heat treated at a temperature of 600° C. for 10 mins. These were blended at a weight ratio of 8:2 and ground fine to obtain a synthetic powder of bismuth oxide/antimony oxide/chromium oxide/boron oxide (whose average particle size is about 2 to 3 μm).

1. temperatureThe mixed powder was heat
2. additiontreated at a temperature of 500° C. for 1 hr
3. temperatureThe mixed powder was heat
4. additiontreated at a temperature of 600° C. for 10 mins

ORD record

ord-7864c291a7724a21b8e421655d891841

Source dataset

uspto-grants-1998_04

DOI

10.6084/m9.figshare.5104873.v1

Patent number

US05739742