Glycidyl acrylate → Glycidyl acrylate 2-hydroxyethyl methacrylate p-acetoxystyrene

Participants

Reaction Steps

A 500 ml three-necked flask was charged with 46.1 g (0.36 mol) of glycidyl acrylate, 15.6 g (0.12 mol) of 2-hydroxyethyl methacrylate, 19.5 g (0.12 mol) of p-acetoxystyrene and 300 ml of methyl isobutyl ketone. A catalytic amount of 2,2′-azobis(methyl 2-methylpropionate) as a radical polymerization initiator was added to the mixture, and polymerization was performed in a nitrogen stream at 80° C. for six hours. The obtained reaction liquid was cooled, and poured in a large volume of heptane, thereby precipitating a polymer. The polymer crystal was collected by filtration, and dissolved in diethylene glycol dimethyl ether. The heptane and methyl isobutyl ketone contained in the solution were distilled off in vacuum, thereby obtaining a diethylene glycol dimethyl ether solution of polymer A2-2 (glycidyl acrylate/2-hydroxyethyl methacrylate/p-acetoxystyrene).