Isoprene → HCID 19842620, compound

HRID 2039306Notes

Reaction equation

HRID 2039306 reaction equation
CN(CCN(C)C)C.[CH2:9]=[CH:10][C:11]1[CH:16]=[CH:15][CH:14]=[CH:13][CH:12]=1.C([Li])CCC.[CH2:22]=[CH:23][C:24](=[CH2:26])[CH3:25]>C1CCCCC1>[CH2:9]=[CH:10][C:11]1[CH:16]=[CH:15][CH:14]=[CH:13][CH:12]=1.[CH2:22]=[CH:23][C:24](=[CH2:25])[CH3:26].[CH2:9]=[CH:10][C:11]1[CH:16]=[CH:15][CH:14]=[CH:13][CH:12]=1

Participants

6

Reactant 4

HCID 6557Isoprene4×HCID 7501Styrene4×HCID 8037N,N,N',N'-TetramethylethylenediamineHCID 178418339Butyllithium2×

Product 1

HCID 19842620HCID 19842620, compound

Reagents, catalysts & solvents 1

HCID 8078CyclohexaneSolvent

Conditions

Temperature
40 °C

Procedure

To a pressure-resistant reactor, 23.3 kg of cyclohexane, 0.8 millimoles of TMEDA and 1.24 kg of styrene were added and stirred at 40° C. Added thereto was 14.1 millimoles of n-butyl lithium, and while the temperature was increased to 50° C., the mixture was polymerized for 1 hour. Next, 43.2 millimoles of n-butyl lithium was further added thereto, and 0.85 kg of isoprene was added thereto continuously over 30 minutes and the polymerization was performed for 1 hour. The degree of polymerization conversion of styrene was 100%. Subsequently, 7.05 kg of isoprene was added to the reactor continuously over 1 hour while the temperature was controlled to maintain 50 to 60° C. After the addition of isoprene was completed, the polymerization was performed for additional 1 hour. The degree of polymerization conversion of isoprene was 100%. Subsequently, 0.85 kg of styrene was added thereto continuously over 30 minutes. After the addition of styrene was completed, the polymerization was performed for additional 1 hour to produce two kinds of styrene-isoprene-styrene block copolymers, which are the block copolymer A and the block copolymer B. The degree of polymerization conversion of styrene was 100%. After that, 114.6 millimoles of methanol was added as a polymerization terminator and mixed well to terminate the reaction. Part of the reaction solution obtained was extracted and subjected to the same measurements as Preparation example 1. The values thereof are shown in Table 2. Subsequent treatments that were the same as those of Preparation example 1 were carried out to recover the block copolymer composition of Preparation example 4.

Workup

  1. additionAdded
  2. temperaturewhile the temperature was increased to 50° C.
  3. customthe mixture was polymerized for 1 hour
  4. waitthe polymerization was performed for 1 hour
  5. temperatureto maintain 50 to 60° C
  6. waitthe polymerization was performed for additional 1 hour
  7. waitcontinuously over 30 minutes
  8. waitthe polymerization was performed for additional 1 hour

Sources & evidence

ORD record
ord-5ff6a3b6fe934152be18b2586b03e574
Source dataset
uspto-grants-2013_11
Patent number
US08578852B2