温度

130 °C

Example 10 describes the preparation of aluminum phosphate sol containing Au nanoparticles. A solution of aluminum s-butoxide (0.19 gm, 0.77 mmol) in methoxyethanol (0.5 ml) is prepared in a vial. It is stirred for 1 hr after addition of mercaptopropyl trimethoxysilane (0.0013 gm, 0.007 mmol). After adding phenyltrimethoxysilane (0.13 gm, 0.66 mmol) and ethylphosphate (0.14 gm, 0.77 mmol), the solution is stirred for another 1 hr. After wrapping the vial with an aluminum foil, the solution is stirred in the presence of gold (III) hydroxide (0.0035 gm, 0.014 mmol) for 3 hrs. Finally, DI water (0.065 gm, 3.6 mmol) is added and the resulting solution is stirred for 48 hrs. The solution is then exposed to sunlight while stirring to form a deep wine red solution, indicating the formation of Au nanoparticles. A thin film formed by casting on a glass plate is clear wine-red. Removal of the volatiles in vacuo followed by heat-treatment in an oven at 130° C./1 hr gives deep wine-red residues (0.18 gm). The dried sol powder (0.04 gm) is stirred in the presence of methoxyethanol (0.5 ml) and phenyltrimethoxysilane (0.01 gm) at 120° C./2 hrs to give a clear wine-red solution that shows no changes in color or optical clarity when allowed to store for over 9 months at room temperature.

1. additioncontaining Au nanoparticles
2. stirringthe solution is stirred for another 1 hr
3. stirringthe resulting solution is stirred for 48 hrs
4. stirringwhile stirring
5. customto form a deep wine red solution
6. customA thin film formed
7. customRemoval of the volatiles in vacuo