To a 5 liter 3-neck round bottom flask were added 233.6 grams (1.35 mole) of methyl acrylamidoglycolate methyl ether (MAGME™), 71.6 grams (1.35 mole) of acrylonitrile, and 246.8 grams of methanol solvent. The comonomer molar mix in this Example was 50:50. The flask was equipped with a water condenser, an Argon inlet and an Argon outlet to a bubbler to ensure that a positive Argon flow was maintained in the reaction vessel throughout the polymerization period. The mixture was mechanically stirred and sparged with Argon at ambient temperature for 2 hours to dissolve the monomers and displace oxygen. To the resulting solution were added 3.05 grams (0.0186 mole) of azobisisobutyrylnitrile initiator, and the stirred solution was warmed to and maintained at 60° C. for 24 hours by means of a hot water bath. The polymer solution was next rotoevaporated to dryness leaving the solid polymer which after vacuum oven drying for 24 hours at 40° C. at about 1 millimeters Hg amounted to 284 grams (93.0 percent of theory). This polymer was used without further purification as a positive charge adjuvant in Liquid Toner 4 prepared in Example VII.

1. customThe flask was equipped with a water condenser, an Argon inlet and an Argon outlet to a bubbler
2. temperaturewas maintained in the reaction vessel throughout the polymerization period
3. customsparged with Argon at ambient temperature for 2 hours
4. dissolutionto dissolve the monomers
5. temperaturethe stirred solution was warmed to and
6. customleaving the solid polymer which after vacuum oven
7. customdrying for 24 hours at 40° C. at about 1 millimeters Hg
8. customThis polymer was used without further purification as
9. additiona positive charge
10. customprepared in Example VII