2-Norbornene → Norbornene tert-Butyl Acrylate

참여 물질

반응 단계

The procedure of Example 2 was followed using 28.2 g (0.30 mol) norbornene, 12.8 g (0.05 mol) tert-butyl acrylate, 100 mL CFC-113, 1.5 g Perkadox® 16N and 60 g (0.60 mol) of tetrafluoroethylene. The product mixture was a clear liquid which was added to excess methanol to precipitate the polymer. There was isolated 28.8 g (29%) of white polymer; GPC (MEK) Mw 16100, Mn 7500, Mw/Mn 2.15; Inh Visc. 0.0862 (MEK); Tg 115° C. Anal. Found: C, 62.32; H, 7.53; F, 18.98. 13C NMR (δ, TCB) 166 to 178 (C═O), 112 to 124 (CF2), 80 (CH), 22 to 54 (remaining carbons). From integrations of appropriate resonances, the polymer composition was found to be 28 mol % TFE, 34 mol % tert-butyl acrylate and 38 mol % norbornene.