HCID 131723423, compound → Ethyl vinyl ether

Participants

Reaction Steps

In 150 ml of 1,4-dioxane were dissolved 15 g of poly(p-hydroxystyrene/isobornyl acrylate) obtained in the above (2) and 6 g of ethyl vinyl ether and 3.2 g of 3,4-dihydro-2H-pyrane and a catalytic amount of pyridinium p-toluenesulfonate was further added thereto, followed by conducting a reaction at room temperature for 24 hours with agitation. After the reaction, the reaction solution was poured into 2000 ml of ion-exchanged water to precipitate out. Crystal was recovered by filtration, washed with water and dried under reduced pressure to give 14.7 g of poly(p-tetrahydropyranyloxystyrene/p-1-methoxyethoxystyrene/isobornyl acrylate) as white powdery crystal. A ratio of p-tetrahydropyranyloxystyrene unit, p-1-methoxyethoxystyrene unit and isobornyl acrylate unit of the obtained polymer was found about 20:50:30 by 1HNMR measurement, and a weight-average molecular weight of the polymer was about 57000 by GPC measurement using polystyrene as a standard.