A master batch was prepared by combining 621.0 g of isooctyl acrylate, 41.4 g of acrylamide, 165.6 g of vinyl acetate, 1.656 g of 2,2′-azobis(2,4-dimethylpentanenitrile) (available from the DuPont Company as Vazo™ 52), 884.52 g of ethyl acetate and 87.48 g of methanol. A 400 g portion of the resulting solution was placed in an amber quart bottle. The bottle was purged for two minutes with nitrogen at a flow rate of one liter per minute. The bottle was sealed and placed in a rotating water bath at 45° C. for twenty-four hours to effect essentially complete polymerization. The copolymer was diluted with 250 g of ethyl acetate/methanol (90/10) to 26.05% solids and had a measured inherent viscosity of 1.27 dl/g in ethyl acetate at a concentration of 0.15 g/dl. Its Brookfield viscosity was 5580 centipoise.

1. customA master batch was prepared
2. customThe bottle was purged for two minutes with nitrogen at a flow rate of one liter per minute
3. customThe bottle was sealed
4. waitplaced in a rotating water bath at 45° C. for twenty-four hours
5. custompolymerization