Stearyl Alcohol → Urethane acrylate

Participants

Reaction Conditions

Reaction Steps

Into a flask similar to the flask in Synthesis Example 1 were charged 60.8 parts of toluene and 8.4 parts of stearyl alcohol (NAA-46), followed by heating of the mixture to 40° C. After the confirmation of thorough dissolution of stearyl alcohol, 50 parts of hexamethylene diisocyanate subjected to isocyanurate modification (TAKENATE D-170N) were charged and the mixture was heated to 70° C. After 30 minutes of the reaction at the same temperature, 0.02 parts of dibutyltin laurate were charged. After 3 hours of maintenance at the same temperature, 28 parts of 2-hydroxyethyl acrylate (HEA), 0.02 parts of dibutyltin laurate, and 0.02 parts of hydroquinone monomethyl ether were charged. The mixture was maintained at 70° C. for 3 hours to complete the reaction, and 25.6 parts of toluene were added to obtain a urethane acrylate containing 50% by weight of solid.