温度

70 °C

This example is directed to the preparation of a typical alkylated phenol component using the process disclosed in U.S. Pat. No. 4,976,882 and alkyl phenol-sulfur condensates produced thereby. Octadecyl phenol was prepared by charging into a four-neck, 5-liter round bottom flask equipped with a mechanical stirrer, 933 grams of phenol (9.93 moles) and 286 grams of Amberlyst 15 catalyst. A reflux condenser, a thermometer, an addition funnel, and a nitrogen inlet tube were attached to the flask and the mixture was heated to 70° C. With stirring under a blanket of nitrogen, 834 grams (3.31 moles) of 1-octadecene was added dropwise over a period of about one hour. The temperature was raised to 90° C and maintained at this temperature for four hours. The reaction mixture was then cooled to 50° C. and filtered to remove the catalyst. The excess phenol was removed by vacuum distillation. The yield was 1,008 grams or 88%. The product has a refractive index of 1.4859 at 25° C., a viscosity of 38.0 cP at 40° C., and a hydroxyl number of 144 mg KOH/g. The infrared spectrum of the product showed absorption bands at 830 and 750 cm-1 m which are characteristic of alkyl phenols. The aromatic substitution pattern was determined by 13C-NMR spectroscopy and showed that the ortho to para ratio was 2.0:1.0. The alkyl substitution pattern was determined by 1H-NMR spectroscopy and showed that the product consisted of 50 mole % 2-substituted alkylate and 50 mole %≥3-substituted alkylate.

1. customby charging into a four-neck, 5-liter round bottom flask
2. customequipped with a mechanical stirrer
3. customA reflux condenser, a thermometer, an addition funnel, and a nitrogen inlet tube were attached to the flask
4. additionwas added dropwise over a period of about one hour
5. temperatureThe temperature was raised to 90° C
6. temperaturemaintained at this temperature for four hours
7. temperatureThe reaction mixture was then cooled to 50° C.
8. filtrationfiltered
9. customto remove the catalyst
10. customThe excess phenol was removed by vacuum distillation
11. customat 25° C.
12. customat 40° C.
13. customabsorption bands at 830 and 750 cm-1 m which