A hundred parts of lanthanum oxide having an average particle diameter of 1 μm, 125 parts of chromium oxide having an average diameter of 1 μm, and 100 parts of ion-exchanged water were put into a polyethylene pot together with zirconia balls, subjected to pulverization and mixing for 20 hours, and then dehydrated by filter pressing. A resultant cake was dried in a drying chamber at 120° C. for 24 hours. The dried cake was ground coarsely, and placed in an aluminacrucible, and heated in air at 1,200° C. for 2 hours to form lanthanum chromite. A hundred parts of the lanthanum chromite powder thus obtained and 100 parts of ion-exchanged water were put into a polyethylene pot together with 200 parts of zirconia balls, and pulverized for 48 hours to provide an average particle diameter of 0.5 μm.

1. additionmixing for 20 hours
2. filtrationby filter
3. customA resultant cake was dried in a drying chamber at 120° C. for 24 hours
4. temperatureheated in air at 1,200° C. for 2 hours