Oxygen → Niobium

Participants

Reaction Steps

NbxCe1-xO2 where x is from about 0.02 to about 0.05 was prepared by the following procedure. A solution of niobium ethoxide was prepared in n-butanol solvent in a low moisture and low oxygen environment to prevent hydrolysis of the niobium ethoxide with moisture present in the air. A partial solution/emulsion of cerium (III) 2-ethyl hexanoate in n-butanol was prepared. Then, the niobium ethoxide solution is admixed with the cerium 2-ethyl hexanoate solution/emulsion in an amount to provide a desired solid solution of about 2 to 5 mole percent niobium dopant. Then, the solution/emulsion mixture was then dried at about 110° C. in air to begin to transform the gel into powder. Next, the dried material was thermally decomposed by calcination at about 650° C. in air to form the solid solution of metal oxides powder agglomerate. The metal oxide powder was then deagglomerated by high frequency vibration through sonication in a MEK-ethanol solution containing a small amount of fish oil to result in an average particle size powder of about 0.8 microns.

Provenance & Evidence