In a glass ball mill container having a volume of 900 mL, 1000 g of 1 mmφ zirconia beads were charged, further 17.0 g (108 mmol) of phenylphosphonic acid (manufactured by Nissan Chemical industries, Ltd.), 8.78 g (108 mmol) of zinc oxide and 231 g of water were mixed, stirred at 170 rpm for 20 hours at room temperature. Then the slurry was separated from zirconia beads, and the separated slurry was filtered, and the wet cake was fully washed with water. Thereafter, the slurry was dried at 150° C. to obtain 23.4 g (yield 98%) of the aimed product as white crystal. The average particle diameter was 1.1 μm with a laser diffraction type particle size distribution meter (manufactured by Seishin Enterprise Co., Ltd., PRO-7000S).

1. additionwere charged
2. customThen the slurry was separated from zirconia beads
3. filtrationthe separated slurry was filtered
4. washthe wet cake was fully washed with water
5. customThereafter, the slurry was dried at 150° C.