4-Methoxyphenol → Urethane acrylate

Participants

Reaction Conditions

Reaction Steps

50 parts of toluene, 50 parts of hexamethylene diisocyanate subjected to isocyanurate modification (“TAKENATE D-170N”), 179 parts of polycaprolactone-modified hydroxyethyl acrylate (“PLACCEL FA5”, trade name, produced by Daicel Chemical Industries, Ltd.), 0.02 parts of dibutyltin laurate, and 0.02 parts of hydroquinone monomethyl ether were mixed and the mixture was maintained at 70° C. for 5 hours. Thereafter, 179 parts of toluene was added to obtain a urethane acrylate having a solid content of 50% by weight. The number of repetitions of a caprolactone unit per one residue of the acrylate monomer in the obtained urethane acrylate is 5.